有效孔径 (%): | 90 |
涂层: | S1: BBAR (8000-12000nm)
S2: DLC Coating |
努氏硬度 (kg/mm2) : | 780 |
平行度(弧分): | <1 |
基底: | Germanium (Ge) |
表面平整度: | λ/10 @ 10.6μm |
表面质量: | 60-40 |
波长范围 (μm): | 8 - 12 |
波长范围 (nm): | 8000 - 12000 |
Coating Abrasion: | AR: Moderate, per MIL-C-48497A Paragraph 4.5.3.3
DLC: Severe, per MIL-C-675C Paragraph 4.5.10 |
Coating Adhesion: | AR: per MIL-C-48497A Paragraph 4.5.3.1
DLC: per MIL-M-13508C Paragraph 4.4.6 |
Coating Humidity: | AR: per MIL-C-48497A Paragraph 4.5.3.2
DLC: ≥24 Hours per MIL-C-675C paragraph 4.5.8 |
Coating Salt Solubility: | AR: N/A
DLC: ≥24 Hours Immersion per MIL-C-675C paragraph 4.5.7 |
Coating Salt Spray: | AR: N/A
≥24 Hours per MIL-C-675C paragraph 4.5.9 |
Coating Solubility and Cleaning: | AR: per MIL-C-48497A Paragraph 4.5.4.2
DLC: N/A |
Coating Temperature (°C): | AR: -80 to +160 per MIL-C-48497A Paragraph 4.5.4.1
DLC: -80 to +160 per MIL-C-48497A Paragraph 4.5.4.1 |
Coating Wiper Durability: | AR: N/A
DLC: ≥5,000 Wipes of Sand/Slurry per TS-1888 |
注意 : | Arrow on substrate edge points towards DLC coated surface |